BASE METAL AND COMBINATIONS
-
Plain carbon steel, some low-alloy steels and iron and steel castings can all be galvanized.
Soldered or brazed components should not be galvanized.
A fabrication consisting of a variety of materials with different surface conditions should be avoided, as this could affect the uniformity and appearance of the coating. Where differing materials are used, grit blasting the entire assembly can minimise any differences which may arise due to differing effects of pre-treatment. Preferably, the fabrication should be of similar steel type throughout.
Steel fabrications that have been subject to heavy cold work (e.g. bent through a tight radius) may be susceptible to strain age embrittlement and should be stress relieved prior to galvanizing.
When the steel to be galvanized is a high-strength steel with crack initiator and a high level of residual stress, consideration should be given to reducing potential for steel cracking to occur. Such a combination is very rare but when it does exist, advice should be sought from Galvanizers Association or reference made to Publication No 40/05, 'Galvanizing structural steelwork - An approach to the management of liquid metal assisted cracking', published by the British Constructional Steelwork Association (BCSA)
SIZE AND SHAPE
-
In recent years, the size and capacity of galvanizing plants has increased significantly. Reference should be made to the Directory of General Galvanizers for and indication of the bath sizes available in the UK and Republic of Ireland. When the length or depth of the item exceeds the size of the bath, special techniques may be employed to facilitate dipping, in this case advice must be sought from the galvanizer.
|
 |
In recent years, the size
and capacity of galvanizing plants has increased significantly. The
capacity of individual galvanizing plants is detailed in the Directory
of General Galvanizers.
|